10C11
Product Description and Uses:
The Schwartz C11 Multi-Use Cement is used for bonding PVC, CPVC and ABS pipes, fittings and rigid surfaces.
Standard Container Sizes
– 118 ml Dauber
Physical Properties: | |
---|---|
Density: | 0.91 – 0.93 g/ml |
Weight Solids: | 14 – 16% |
Flashpoint: | -17°C |
Hydrostatic Burst Strength: | 400 psi (23°C); 200 psi (82°C) per ASTM F 493 |
Appearance: | Clear liquid |
Shelf Life: | 12 months unopened |
Suggested Uses: |
For PVC, CPVC and ABS plastic pipes, fittings and rigid surfaces. |
Application Tools: |
Dauber or brush. |
Clean-up Solvent: |
VC100 |
Pot Life: |
NA |
Safety and Technical Data Sheets for Download
TDS
TDS 10C11 – C11 Multi-use Solvent Cement (pdf)
SDS
SDS 10C11 – C11 Clear Multi-use Cement (pdf)
SDS 10C11 – C11 Clear Multi-use Cement (pdf – French)
Set Times:
Handle newly assembled joints carefully until cement has gone through its set period.
Recommended set time is temperature dependent:
– Minimum 30 minutes at 15ºC to 38ºC
– Minimum 1 hour at 7ºC to 15ºC
– Minimum 2 hours at 0ºC to 4ºC
Cure Times: | ||||||
---|---|---|---|---|---|---|
Test Pressures For Pipe Sizes 1⁄2″ to 1-1⁄4″ |
Test Pressures For Pipe Sizes 1-1⁄2″ to 3″ |
Test Pressures For Pipe Sizes 3-1⁄2″ to 8″ |
||||
Temperature Range During Cure Period |
Up to 180 psi |
Above 180 to 370 psi |
Up To 180 psi |
Above 180 To 315 psi |
Up To 180 psi |
Above 180 To 315 psi |
15°C – 38°C |
1 hr. | 6 hr | 2 hr. | 12 hr. | 8 hr. | 24 hr. |
4°C – 15°C |
2 hr. | 12 hr. | 4 hr. | 24 hr. | 16 hr. | 48 hr. |
Storage:
Store indoor at room temperature, away from heat, ignition sources,
open flames and direct sunlight.
Warning:
Avoid open flames, turn off all pilot lights, ensure that work
area is properly ventilated.
Soiled rags and waste products may contain combustible liquids
or vapours and SPONTANEOUSLY COMBUST, dispose in accordance with
local regulations.
Refer to SDS for information on safe use of this product.